The difference of low carbon steel vessels in IEC60335-2-6 version 2004 and version 2014


The low-carbon steel test vessels referred in this article is produced in accordance with the requirements of the standard IEC60335-2-6 Figure 102 for testing induction hob elements. In the standard, the wall thickness (A), base thickness, the maximum concavity(C), the diameter (d) and the height (e) are all have detail instructions, and the description is as follows:

The vessels are made of low carbon steel having a maximum carbon content of 0.08%. It is cylindrical without metallic handles or protrusions. The diameter of the flat area of the base of the vessel shall be at least the diameter of the cooking zone. The base of the vessel shall not be convex. The concavity of the base of the vessel shall not exceed 0.6% of its diameter.

 


But for the base thickness, the standard IEC60335-2-6 in version 2014 and version 2004 are slightly different. In the 2004 version, the bottom thickness of all sizes is required to be 2mm±0.5mm. However, in the 2014 version, the requirements for base thickness of each size are different, vessels with d<145mm, the base thickness is required to be 2mm±0.5mm; d=145mm to 240mm, the base thickness is required to be 3mm±0.5mm; d>240mm, and the base is required to be 5mm±0.5mm.

 

The low carbon steel test vessels also can meet the requirement of IEC60335-2-9 figure 104, but the standard IEC60335-2-9 in version 2002 and version 2019, the base thickness has no difference, both are 2mm±0.5mm.

 

Therefore, please confirm the standards to be met with the sales when inquiring, so that we can quote you correctly.

标签：

评论

发表评论

此博客中的热门博文

JIS D0203 rain nozzle and spray nozzle test chamber

https://www.pegotester.com/JISD0203_rain_and_spray_test_chamber.html The spray nozzle and rain nozzle test chamber is designed to meet the test requirements of JISD0203 R1/R2 rain test and S1/S2 spray test. The rain nozzle has 2 holes and spray nozzle has 40 holes. Type Symbol Test Purpose Test Method Rain Test R1 Auto parts against water direct contact water pressure: 0.01Mpa, water flow: 1.9L/min, water temperature: ordinary temperature, test time: 10min R2 Auto parts against rain or spray water   indirect contact water pressure: 0.03Mpa, water flow: 3.2L/min, water temperature: ordinary temperature, test time: 10min Spray Test S1 Auto parts against rain or jet water direct contact water pressure: 0.10Mpa, water flow: 24.5L/min, water temperature: ordinary temperature, test time: 30min S2 Auto parts against riptide water pressure: 0.30Mpa, water flow: 39.2L/min, water temperature: ordinary temperature, test time: 1h  
发表评论
阅读全文

UL746A High Current ARC Ignition Test Apparatus 32.5A/COSφ0.5

UL746A High Current ARC Ignition Test Apparatus 32.5A/COSφ0.5   1.  Introduction: The high current arc ignition tes t apparatus is designed according to  IEC60950-1:2001  clause 4.7.3.6 , BS/EN60950-1:2001, BS7002:2001, GB4943-2001 and UL746A, IEC60947.1:1999, GB/T14048.1-2000, IEC730.1:1993, GB14536.1-1998 and etc..  It ’ s used to measure and assess  solid insulating material against to resistance to ignition from arcing electrical sources. A power 240V(AC)/60Hz is to be supplied to the test electrodes  (fixed electrode and movable electrode) , a series (inductive-resistive) air core impedance is to be provided to yield a short circuit current of 32.5A and a power factor of 0. 5. The sample is be to positioned with the electrodes making initial contact on the surface of the sample, the circuit is to be energized and the cyclic arcing started. The timing of arcs is to be adjusted to a rate of 40 arcs/min, the rate of electrode separation is to be 254±...
发表评论
阅读全文

The material of standardized cookware in EN60350-2 version 2018 and version 2013

The standardized cookwares referred in this article are designed according to EN(IEC)60350-2 table (Z)3. The diameter of the cookware bottom (outside), diameter of the lid, lid hole circle diameter, number of holes on the circle, total cookware height (outside) and flatness of cookware bottom are specified in table (Z)3. The materials of side wall, cookware bottom and lid are different. In version 2018, the side wall of cookware is made of stainless steel AISI type 304, the cookware bottom is made of stainless steel AISI type 430, and and the lid is made of aluminium. In version 2013, the side wall of cookware is made of 1.4301 stainless steel, the cookware bottom is made of stainless steel 1.4016, and the lid is made of aluminium. Items Version 2018 Version 2013 Remark material thickness material thickness Side wall   stainless steel AISI  304 1mm±0.05mm 1.4301 stainless steel 1mm±0.05mm C ylindrical without handles or protrusions. Cookware bottom stainless steel AISI  ...
发表评论
阅读全文